The effects of mouthrinses on dental resin composites have been investigated extensively. However, there is little information available regarding the effects of ‘newly developed mouthrinse’ formulations on the microhardness of different monomer based composite systems. Therefore, the aim of this study was to investigate the effect of a novel potassium-oxalate containing desensitizing mouthrinse on the microhardness of different monomer based composite materials. A hundred and twenty specimens (6mm in diameter and 2mm in height) were prepared for composite resin groups (methacrylate based, DX-511 monomer based and silorane monomer based) and for storage solution groups (artificial saliva and potassium oxalate-containing tooth-desensitizing mouthrinse). After allowing post-polimerization the baseline Knoop microhardness measurements for all specimens were recorded. The specimens were stored in 20 mL mouthwash and artificial saliva for 12 hours at 37ºC. The post-immersion microhardness values of all specimens were also recorded. Data were subjected to ANOVA/Scheffe’s test at a significance level of 0.05. The intra group (pre and post immersion values) comparison of the mean microhardness values of the specimens was done using Wilcoxon signed rank test. The microhardness of the silorane based composite was not affected significantly (p>0.05). The hardness values of the DX-511 monomer based composite and the methacrylate based composite exhibited a slight but not significant microhardness change compared to the baseline values (p>0.05). Studies reported that the effect of mouthrinses on microhardness changes of composite resins may be material dependent, and the hardness change susceptibility of a restorative material may be attributed to its resin matrix or filler type. However, dental monomers as well as the oral care products have an ever-evolving technology and future studies should consider newer products. Potassium oxalate containing mouthrinses, especially alcohol-free ones, may be used safely with dental composites with newly developed low-shrink monomer compositions.