The purpose of this study is to determine if the duration of exposure to the halogen overhead dental chair light has an effect on shear bond strength (SBS) of metal orthodontic brackets. One hundred twenty extracted human lower incisor teeth were divided into six groups (n=20/group). Each group was assigned a predetermined duration of exposure to the halogen dental chair light, set at a fixed distance, before being cured. Light exposure times of 0 minutes (Group 1-Control), 1 minute (Group 2), 2.5 minutes (Group 3), 5 minutes (Group 4), 10 minutes (Group 5), and 15 minutes (Group 6) were tested. Each tooth was subjected to an exclusion criteria examination, scrubbed of all debris, and imbedded in a PVC-stone fixture with the crown of the tooth exposed above the stone surface. All groups had orthodontic brackets bonded with the same materials and process, then light cured for 6 seconds using the Valo LED curing unit after their designated light exposure time. Groups were tested using an Instron E-1000 universal testing machine with a shear load test set at a speed of 1mm/min using a knife-edged chisel. Data was analyzed using a one-way ANOVA test. The Adhesive Remnant Index (ARI) was scored under 10x magnification. The ARI data was analyzed using the Chi-square test (p-value < 0.05). All control and experimental groups for each specific tooth type tested resulted in SBS within or above the clinically acceptable range. Statistically significant differences (p<.05) were found between the control and experimental groups for dental chair light exposure times of 5 minutes, 10 minutes and 15 minutes. A chi-square test determined that there was statistical significance when evaluating the frequency of ARI scores when light exposure duration was greater than 5 minutes. It can be concluded that dental chair light exposure in the 5 minute, 10 minute and 15 minute groups produced higher shear bond strength than those of the control, 1 minute and 2.5 minute groups. The dental chair light is capable of initiating polymerization and causing higher bond strengths than the clinical acceptability of 5.8-7.9 MPa, thus continued dental chair light exposure over 5 minutes is not recommended. The ARI analysis revealed that as bond strength increased, the fracture pattern shifted from most remaining adhesive attached to the tooth toward that attached to the bracket.