Role of coefficient of thermal expansion on bond strength of ceramic veneered yttrium-stabilized zirconia

Mostra el registre parcial de l'element

dc.contributor.author Juntavee, Niwut es
dc.contributor.author Dangsuwan, Chollada es
dc.date.accessioned 2018-05-23T09:25:47Z
dc.date.available 2018-05-23T09:25:47Z
dc.date.issued 2018 es
dc.identifier.citation Juntavee, Niwut ; Dangsuwan, Chollada. Role of coefficient of thermal expansion on bond strength of ceramic veneered yttrium-stabilized zirconia. En: Journal of Clinical and Experimental Dentistry, 10 3 2018: 279-286 es
dc.identifier.uri http://hdl.handle.net/10550/66344
dc.description.abstract Incompatible coefficient of thermal expansion (CTE) is supposed to be a reason for chipping of ceramic veneered zirconia. This study evaluates the effect of veneering ceramic at varied CTE on bond strength to zirconia. Zirconia disks (Z, Ø 10 mm, 1.0 mm thickness) were prepared from Y-TZP (Cercon®) and sintered at 1350°C for 6 hours. All zirconia disks were veneered with ceramics ((Ø 7.0 mm, 1.5 mm thickness) with varied CTE including VITADur® alpha (VD?), VITAVM®7 (VM7), VITAVM®9 (VM9), Cercon® ceramkiss (CCK), IPSe.max® ceram (IeC), and IPS dSIGN® (IdS) (n=15). The specimens were thermo-cycled (5-55 °C, 500 cycles) prior to determine the shear bond strength on a universal testing machine. The veneering ceramic and zirconia rods (Ø 4 mm, 30 mm length) were prepared for CTE evaluation. ANOVA and Tukey?s multiple comparisons were used to determine the statistically significant difference (?=0.05). Weibull analysis was applied for survival probability, Weibull modulus (m), and characteristics strength (?o) of the shear bond. The interfaces were microscopically examined. The phase transformation of zirconia was determined using X ray diffraction. The mean±sd (MPa), m, and ?o of bond strength were 20.45±2.32, 9.25, and 21.53 for Z-VD?, 19.47±4.53, 4.66, and 20.31 for Z-VM7, 21.05±3.96, 5.61, and 21.88 for Z-IeC, 25.85±2.74, 9.93, and 27.15 for Z-VM9, 25.82±4.39, 6.27, and 27.06 for Z-CCK, and 2.96±0.73, 4.11, and 3.28 for Z-IdS. The CTE (×10-6/°C) were 10.80, 7.83, 7.87, 9.86, 9.93, 10.03, and 12.95 for Z, VD?, VM7, IeC, VM9, CCK, and IdS. The bond strength was significantly affected by the CTE difference (p<0.05). The t?m phase transformation related with the CTE difference. The CTE?s differences induced stress that affected the bond strength. CTE?s compatibility of veneering ceramic to zirconia is crucial for enhancing the bond strength. The CTE difference approximately 0.77-0.87×10-6/°C was recommended. es
dc.title Role of coefficient of thermal expansion on bond strength of ceramic veneered yttrium-stabilized zirconia es
dc.type journal article es_ES
dc.subject.unesco UNESCO::CIENCIAS MÉDICAS es
dc.identifier.doi 10.4317/jced.54605 es
dc.type.hasVersion VoR es_ES

Visualització       (2.134Mb)

Aquest element apareix en la col·lecció o col·leccions següent(s)

Mostra el registre parcial de l'element

Cerca a RODERIC

Cerca avançada

Visualitza

Estadístiques